Apparatus for the filtration of molten metal in a crucible type furnace

ABSTRACT

An improved apparatus for the filtration of molten metal for use in the production of castings is disclosed in which a ladling crucible provided with a ceramic foam filter is employed in a furnace type crucible to remove impurities.

BACKGROUND OF THE INVENTION

The present invention relates to the filtration of molten metal.

Molten metal, particularly molten aluminum, in practice generallycontains entrained and dissolved impurities, both gaseous and solid,which are deleterious to the final cast product. The impurities mayoriginate from several sources. For example, the impurities may includemetallic impurities such as alkaline and alkaline earth metals, andoccluded hydrogen gas and dissolved surface oxide films which havebecome broken up and are entrained in the molten metal. In addition, theinclusions may originate as insoluble impurities, such as carbides,borides and others or eroded furnace and trough refractories.

In typical sand, permanent mold and die casting foundries, it is commonpractice to use a pot or crucible type melting and holding furnace incapacity from 300 lbs to 1500 lbs of molten aluminum alloy. Depending onthe type of operation, this furnace may be filled with the molten alloyfrom a larger furnace, or, the cold alloy may be added to the cruciblefurnace and melted therein. After the furnace is full of molten metal,it is common practice to treat the melt by fluxing with Cl₂, N₂,mixtures thereof, or C₂ Cl₆ and an added additional grain refiner in theform of salts or a 5% Ti-1% B aluminum alloy hardener. The melt is thenadjusted to the desired temperature and pouring of castings is allowedto begin.

Pouring is usually carried out with hand carried or manipulated ladles.The ladle is sized to hold slightly more metal than that required topour one or more of the molds. The operator dips the ladle into the meltand fills it, wipes any skim from the melt surface and ladle lip andpours the molten metal into the molds. The residue of metal left in theladle is dumped back into the parent melt in the furnace. Numerous poursare made in this manner until 1/2 to 2/3 of the molten metal has beencast. The repeated operation of bailing, pouring and dumping backresults in the generation and entrainment of large quantities of oxidefilms and particulate in the parent melt.

The foundry alloy ingot used in preparing melts as described above arenormally cast by a primary or secondary producer in an inline piggingmachine. This operation involves the free fall of metal into the pigmold cavity. In addition, the melt treatment practices generally used inthe production of the foundry alloy ingot are less than adequate. As aresult, the ingot usually contains entrained oxide films andnon-metallic particulate.

The oxides generated and entrained in the melt as described above canand often do produce defects in the resulting castings that are a causefor rejection. This is particularly true in specification type work forcritical applications where the foundryman must meet specifiedradiographic standards.

The use of proper melt treatment and fluxing practices by the foundrymanhelps minimize inclusion problems. However, there is no method presentlyavailable for insuring that metal ladled from the crucible type furnaceand poured into the mold is substantially free of undesirablenon-metallics.

It is naturally highly desirable to filter the molten metal in thecrucible type furnace in order to remove or minimize impurities in thefinal cast product especially, for example, when the resultant metal isto be used in a decorative product, such as decorative trim, or productsbearing critical specifications, such as aircraft forgings andextrusions, and light gauge foil stock. Impurities as aforesaid causeloss of properties such as tensile strength and corrosion resistance inthe final solidified alloy and lead to degradation of processingefficiency and loss of properties in the final cast product.

One conventional method of filtering in crucible type melting operationsis disclosed in Volumn 3 of "Aluminum" published by American Society ofMetals, 1967, page 35. This procedure requires the placing of a filterplate of porous refractories or carbon vertically in a crucible therebydividing the crucible into two compartments, one for charging withmolten metal and the other for ladling the molten metal. This procedurehas a number of drawbacks, among them, the filter of porous refractoriesor carbon is not efficient in removing the aforesaid oxide films andnon-metallic particulate. Furthermore, the system is not particularlyefficient because due to the limited surface area of the filtersemployed, the system must be continually shut down in order to replacethe filters. Finally, there is a problem in sealing the filter in thecrucible so as to prevent leakage of the molten metal around thefiltering system.

An alternative to the above crucible filtering techniques as set outabove is diclosed in U.S. Pat. No. 3,729,097. This procedure requiresplacing a free floating member with an aperture at the bottom, which iscovered with a glass cloth filter, in a molten metal thereby allowingthe metal to float up through the filter into an inclosure where it isremoved by a ladle. Again, this procedure suffers from a number ofdeficiencies, for example, the limited size of the filter requires thatit be replaced frequently while the filter material itself is notefficient in removing oxide films and non-particulate impurities.

Porous ceramic foam materials are known to be particularly useful infiltering molten metal, as described in U.S. Pat. No. 3,893,917 for"Molten Metal Filter" by Michael J. Pryor and Thomas J. Gray, patentedJuly 8, 1975 and also as described in U.S. Pat. No. 3,962,081 for"Ceramic Foam Filter" by John C. Yarwood, James E. Dore and Robert K.Preuss, both of which patents are assigned to the assignee of thepresent invention.

Porous ceramic foam materials are particularly useful for filteringmolten metal for a variety of reasons included among which are theirexcellent filtration efficiency, low cost, ease of use and the abilityto use same on a disposable, throwaway basis. The fact that theseceramic foam filters are convenient and inexpensive to prepare and maybe used on a throwaway basis allows for the development of means foreasily assembling and removing porous molten metal filters from acrucible type melting furnace while providing a highly efficientfiltration assembly.

Accordingly, it is the principal object of the present invention toprovide an improved method and apparatus for the filtration of moltenmetal in a crucible type melting furnace.

It is a particular object of the present invention to provide animproved removable filter means for use in the filtration of moltenmetal in a crucible type furnace.

It is still a further object of the present invention to provideimprovements as aforesaid which are convenient and inexpensive toutilize and which result in high filtration efficiency.

Further objects and advantages of the present invention will appearhereinbelow.

SUMMARY OF THE INVENTION

In accordance with the present invention, it has been found that theforegoing objects and advantages may be readily obtained.

The present invention provides a highly efficient filtration assemblywhich utilizes a conveniently removable filter means. The removablefilter means of the present invention is easily assembled anddisassembled in the filtration assembly and enables one to obtainexcellent filtration efficiency.

In accordance with the present invention, a crucible type furnace isprovided with a rigid, readily replaceable filter means for thefiltration of molten metal having an open cell structure characterizedby a plurality of interconnected voids. The filter means is preferably aceramic foam filter plate with interconnected voids being surrounded bya web of ceramic wherein said filter means is positioned in the cruciblefurnace so as to enable molten metal to pass through the filter meansinto an area which separates filtered metal from the non-filtered metal.

Accordingly, it is also seen that the present invention provides animproved apparatus for the filtration of molten metal in crucible typefurnaces by providing a more efficient, readily replaceable, rigidfilter assembly of greater surface area than heretofore known. Thepresent invention, as indicated above, provides considerable advantagesin the filtration of molten metal, especially aluminum. Thus, forexample, the present invention enables one to filter molten metal in acrucible with a conveniently removable filter means which may be easilyand quickly inserted in the filtration apparatus. In accordance with thepreferred embodiment of the present invention, when a ceramic foamfilter is utilized, extremely high filtration efficiencies are obtainedand these efficiencies are obtained utilizing a disposable filter whichcan be readily inserted and removed from the filter apparatus.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a side view of a first embodiment of the present invention.

FIG. 2 is a second embodiment of the present invention.

FIG. 3 is a third embodiment of the present invention.

FIG. 4 is a forth embodiment of the present invention.

DETAILED DESCRIPTION

FIGS. 1-4 illustrate the various embodiments of the present inventionwherein a typical pot or crucible type furnace 1 is provided with amelting crucible 2 which contains the parent melt 3 of molten metal.

FIG. 1 illustrates one embodiment of the present invention whereinfiltration of the molten metal is accomplished by providing a freefloating ladling crucible 4 with a ceramic foam filter element 5 in thebottom thereof which is appropriately sealed therein by means of seals6. When the ladling crucible 4 with the filter element 5 sealed in placeby seals 6 is immersed in the melt 3, the filter element 5 will primeand molten metal will flow through the filter element 5 into and fillthe cavity 7 of the ladling crucible 4. As the molten metal passesthrough the filter element 5, substantially all of the entrained oxidefilms and non-metallic particulate are removed.

The bottom of ladling crucible 4 is provided with a circumferentiallybevelled portion or aperture 8 extending around the periphery thereofwhich mates with a corresponding bevelled wall peripheral surface 9 ofthe filter element 5. The bevelled peripheral surface 9 of filterelement 5 is provided with a resilient sealing means 6 thereon which isresistant to molten metal. The filter element 5 and sealing means 6 areinserted in the ladling crucible 4 so that the filter element sealingmeans assembly engages the bevelled wall surface of ladling crucible 4.

The ladling crucible 4 and filter element 5 may be of any convenientshape such as round, square, hexagonal or the like. The filter 5 issealed in place by means of resilient seal 6 so that the filter elementmay be readily inserted and easily removed in the ladling crucible 4 byvertical pressure. Preferably, the bevelled peripheral surface of theladling crucible 4 is bevelled at an angle of from 2° to 20° and thefilter element is preferably provided with a bevelled surface 9corresponding thereto at an angle of from 2° to 20°.

Since the filter element 5 of the present invention is designed to be athrowaway item, it is essential to provide an effective means of sealingthe filter element 5 in place in the bottom of ladling crucible 4. It ispreferred to seal the filter plate in place using a resilient seal meansor gasket type seal 6 as illustrated in FIG. 1, which peripherallycircumscribes the filter element at the bevelled portion thereof. Thegasket type seal must be of a material that is resistant to moltenaluminum alloys and resilient at elevated temperatures. Resiliency isrequired to make a metal tight seal between the filter element 5 and theladling crucible 4 and hold the filter element securely in place.Typical seal materials include fibrous refractory type seals of avariety of compositions. Some typical seal compositions are, but notlimited to: (1) a seal containing about 45% alumina, 52% silica, 1.3%ferric oxide and 1.7% titania; (2) a seal containing about 55% silica,40.5% alumina, 4% chromia and 0.5% ferric oxide; and (3) a sealcontaining about 53% silica, 46% alumina and 1% ferric oxide.

The body of ladling crucible 4 may be made of dense graphite but mayalso be formed of other materials which are substantially unaffected bymolten aluminum, provided that such material is less dense than moltenaluminum. The weight of the ladling crucible 4 may be increased by meansof an iron ring embedded in the graphite so as to be protected fromcontact by molten aluminum. The additional weight enables the filterelement 5 to sink further into the molten metal, however, the necessityof the additional weight is usually not necessary.

In the preferred embodiment, filter element 5 is a ceramic foam filteras described in the aforesaid U.S. Pat. Nos. 3,893,917 and 3,962,081. Inaccordance with the teachings of the aforesaid patents, the ceramic foamfilter has an open cell structure characterized by a plurality ofinterconnected voids surrounded by a web of ceramic material. Theceramic filter has an air permeability in the range of from 400 to 8,000× 10⁻⁷ cm², preferably from 400 to 2,500 × 10⁻⁷ cm², a porosity or voidfraction of 0.80 to 0.95 and from 5 to 45 pores per linear inch,preferably from 20 to 45 pores per linear inch. The molten metal flowrate through the filter should be 25 to 50 cubic inches per square inchof filter area per minute. The ceramic foam filter described in U.S.Pat. No. 3,962,081 is particularly suitable in the present inventionsince it is low cost and may be readily employed on a throwaway basis.Furthermore, this filter is surprisingly effective in the filtration ofmolten metal, especially aluminum, at a low cost achieving surprisingfiltration efficiency with considerable flexibility.

The ceramic foam filter may be prepared in accordance with the generalprocedure outlined in U.S. Pat. No. 3,893,917 wherein an aqueous ceramicslurry is prepared and the foam material impregnated therewith so thatthe web thereof is coated therewith and the voids substantially filled.The impregnated material is compressed so that a portion of the slurryis expelled therefrom and the balance uniformly distributed throughoutthe foam material. The coated foam material is then dried and heated tofirst burn out the flexible organic foam and then sinter the ceramiccoating thereby providing a fused ceramic foam having a plurality ofinterconnected voids surrounded by a web of bonded or fused ceramic inthe configuration of the flexible foam. Naturally, a wide variety ofceramic materials may be chosen depending upon the particular metal tobe filtered. Preferably, a mixture of alumina and chromia is employed;however, these materials may naturally be utilized separately or incombination with other ceramic materials. Other typical ceramicmaterials which may be employed include zirconia, magnesia, titaniumdioxide, silica and mixtures thereof. Normally, the slurry contains fromabout 10 to 40% of water and one or more rheological agents, binders, orair setting agents.

In operation, the molten metal which passes through the filter element 5into the cavity 7 of the ladling crucible 4 is ladled from the cavity 7for pouring the sand, permanent mold or die casting. Any residual moltenmetal remaining in the ladle after pouring the castings is then dumpedback into the parent melt 3 into the furnace crucible 2. As the moltenmetal is ladled from the cavity 7 of the ladling crucible 4, adifference in the metallostatic head or metal level 10 is createdbetween the molten metal 3 in the furnace crucible 2 and the ladlingcrucible 4. This difference in metallostatic head 10 causes molten metalto flow through the filter element 5 and equalize the molten metal level10 in the furnace crucible 2 and the ladling crucible 4. In thisfashion, additional metal is filtered for the pouring of castings.

Ladling of metal from the ladle crucible 4 for pouring or casting canproceed until the overall metal level 10 and the ladling crucible cavity7 drops to a point where the ladle can no longer be filled. Byproceeding in this fashion, as described above, only filtered moltenmetal substantially free of oxide films and particulate is ladled andpoured into the casting molds.

Several modes of operation, namely, semi-continuous, or batch type maybe employed with the present invention.

In the semi-continuous operation, the furnace crucible 2 would be filledwith molten metal 3 with a larger holding furnace, the pre-heatedladling crucible 4 inserted in the melt, and ladling in casting started.When the melt 3 in the furnace crucible 2 reaches a predeterminedminimum level, the furnace crucible 2 would be refilled with moltenmetal 3 from the larger holding furnace and casting would be resumed.This cycle would be continued several times until (1) the furance wasshut down at the end of the day, or (2) plugging of the filterexcessively delayed refilling of the ladling crucible between pours. Thesemi-continuous operation requires that melt treatment, i.e., degassing,and the addition of grain refiners be carried out in the larger holdingfurnace prior to transfer of the molten metal to the crucible furnace 2.

In a typical batch type operation the aluminum alloy pig would becharged to and melted in the furnace crucible 2. Once the molten grainrefiners are added, the melt is degassed and the surface thereofskimmed. The preheated ladling crucible 4 with the filter element 5would then be inserted into the melt 3. Casting would proceed until themelt level 10 in the furnace crucible 2 reached a minimum level. At thistime casting would be stopped, the ladling crucible 4 removed and theabove cycle repeated. With the batch type operation it will be necessaryto insert a new filter element 5 in the ladling crucible 4 after eachrun. It is expected that the ladling crucible 4 itself would last for anumber of casting runs.

The filter element and ladling crucible design of the present inventionoffer significant improvements over other filtration methods heretoforeknown. The use of ceramic foam as a filter element results in superioreffective filtration of the molten metal over previously known filtermaterials. The mating bevelled portions of the filter element and theladling crucible allow for easy and effective insertion and removal ofthe filter element. Since the filter element of the present invention isdesigned to be a throwaway item, it is essential that the element bereadily inserted and removed from the ladling crucible while maintainingan effective seal between the bevelled faces of the aforesaid elements.

An alternative form of a ladling crucible and filter assembly is shownin FIG. 2. In this case, the ceramic foam filter element 11 makes upsubstantially the total surface area of the ladling crucible 12. A freefloating ring 13, which may be formed of graphite or other suitablematerial, is provided with a circumferential bevelled surface 14 similarto that described in the previous embodiment of FIG. 1. The ceramic foamfilter element 11 is provided with a corresponding mating bevelledperipheral surface 15 which mates with the aforesaid bevelled surface onfree floating ring 13. Appropriate seal means 16 is provided on thebevelled surface of filter element 11 in the same manner as previouslydescribed for the embodiment of FIG. 1. Thus, the ceramic foam filter isreadily replaceable within the ring member in the same manner asdescribed in the previous embodiment. Furthermore, the filter andcrucible assembly may be of any given shape such as round, square,hexagonal or the like. The mode of operation in this embodiment is thesame as previously described above.

The embodiment of FIG. 2 has certain advantages over that of FIG. 1 andthe prior art, the primary advantage being a substantial increase in thesurface area of filter medium. By employing ceramic foam material forthe filter element in the embodiment of FIG. 2, a sturdy rigid structureis obtained which could not be accomplished by using previously knownglass cloth filters.

A third embodiment of the present invention is illustrated in FIG. 3.The filter and ladle crucible assembly is indentical to that set forthfor the embodiment of FIG. 2. As can be seen from FIG. 3, the ladlecrucible assembly is not allowed to free float but rather is freelyslidable and supported for vertical movement on support structure 17.Ring 13 is provided with track 18 which mates with a like track onsupport 17. As the level of molten metal in the furnace crucible 2 isdiminished, the ladling crucible and filter assembly 12 will slide downthe support 17 to the appropriate level. This embodiment is advantageousin that there is no danger that during the ladling operation the ladlingcrucible may be tipped over.

An additional embodiment of the ladling crucible, not illustrated, maybe formed with only the side walls of the ladling crucible being made ofceramic foam while the bottom and top ring of the crucible are made ofgraphite or other suitable material as previously disclosed.

A further embodiment of the present invention is illustrated in FIG. 4.As can be seen with respect to FIG. 4, a ceramic foam filter 19 acts asboth the filter and ladling crucible. The filter in FIG. 4 isillustrated as a truncated cone, however, it may be any appropriateshape such as rectangular, cylindrical or the like. The base of furnacecrucible 2 is provided with a cut out groove 20 in the same shape asthat of filter element 19. The bottom of filter element 19 is providedwith seals 21 of the type previously described. The base of filterelement 19 is fitted into the corresponding mating groove 20 in the baseof furnace crucible 2 and sealed therein by the seals 21. The filter andgroove are bevelled in the same manner as previously described. Again,as is the case in the previous embodiments, the filter element 19 isreadily replaceable within the furnace crucible 2. This embodiment has anumber of advantages over the previously described prior art. Firstly,the surface area of the filter element is greatly improved. In addition,the rigid structure of the filter element would prevent any tipping ofthe crucible which otherwise might occur. Finally, the embodiment ofFIG. 4 eliminates the need for any graphite crucible member which wouldnormally have to be replaced due to wear.

It is to be understood that the invention is not limited to theillustrations described and shown herein, which are deemed to be merelyillustrative of the best modes of carrying out the invention; and whichare susceptible of modification of form, size, arrangement of parts anddetails of operation. The invention rather is intended to encompass allsuch modifications which are within its spirit and scope as defined bythe claims.

What is claimed is:
 1. An improved filtration apparatus for filteringmolten metal used in the production of castings comprising:a furnacecrucible; means to charge said furnace crucible with molten metal; aladling crucible positioned in said molten metal within said furnacecrucible; said ladling crucible being formed at least in part of amaterial having an open cell structure characterized by a plurality ofinterconnected voids; and wherein said ladling crucible includes meansto vertically slide within said furnace crucible on a support.
 2. Anapparatus according to claim 1 wherein said slide means is in the formof a track adapted to mate with a similar track on said support.
 3. Anapparatus according to claim 2 wherein said material is ceramic foam. 4.An apparatus according to claim 3 wherein said ceramic foam material hasan air permeability in the range of 400 to 8,000 × 10⁻⁷ cm², a porosityof 0.80 to 0.95 and a pore size of 5 to 45 pores per linear inch.
 5. Animproved filtration apparatus for filtering molten metal used in theproduction of castings comprising:a furnace crucible; means to chargesaid furnace crucible with molten metal; a ladling crucible positionedin said molten metal within said furnace crucible; said ladling cruciblecomprises a member having an open top, side wall means and a bottom;said side wall means of said ladling crucible being formed of a materialhaving an open cell structure characterized by a plurality ofinterconnected voids; said open top being formed of an imperforatedmaterial; and wherein said open top has a bevelled peripheral surfaceadapted to receive said side wall means.
 6. An apparatus according toclaim 5 wherein said material is ceramic foam.
 7. An apparatus accordingto claim 6 wherein said ceramic foam material has an air pemeability inthe range of 400 to 8,000 × 10⁻⁷ cm², a porosity of 0.80 to 0.95 and apore size of 5 to 45 pores per linear inch.
 8. An apparatus according toclaim 7 wherein said ladling crucible includes means to vertically slidewithin said furnace on a support.
 9. An apparatus according to claim 8wherein said slide means is in the form of a track adapted to mate witha similar track on said support.
 10. An improved filtration apparatusfor filtering molten metal used in the production of castingscomprising:a furnace crucible; means to charge said furnace cruciblewith molten metal; ladling crucible means positioned in said moltenmetal within said furnace crucible; said ladling crucible means beingformed at least in part of a material having an open cell structurecharacterized by a plurality of interconnected voids; and wherein saidladling crucible means is adapted to removably mate with said furnacecrucible so as to form a ladling compartment so that said charged moltenmetal passes through said ladling crucible means and is filteredthereby.
 11. An apparatus according to claim 10 wherein said furnacecrucible comprises a base, said base being formed with a groove havingbevelled side wall surfaces adapted to receive said ladling cruciblemeans.
 12. An apparatus according to claim 11 wherein said ladlingcrucible means has a bevelled peripheral surface adapted to removablymate with said bevelled surface of said groove in said base andincluding a resilient seal means on said bevelled crucible surface, saidseal means being resistant to molten metal.
 13. An apparatus accordingto claim 10 wherein said ladling crucible means is in the form of ahollow enclosure wherein the interior of said hollow enclosure formssaid ladling compartment.
 14. An apparatus according to claim 13 whereinsaid material is ceramic foam.
 15. An apparatus according to claim 14wherein said ceramic foam material has an air permeability in the rangeof 400 to 8,000 × 10⁻⁷ cm², a porosity of 0.80 to 0.95 and a pore sizeof 5 to 45 pores per linear inch.
 16. An improved filtration apparatusfor filtering molten metal used in the production of castingscomprising:a furnace crucible; means to charge said furnace cruciblewith molten metal; a ladling crucible positioned in said molten metalwithin said furnace crucible; said ladling crucible comprises a memberhaving an open top, side wall means and a bottom, said bottom beingformed of material having an open cell structure characterized by aplurality of voids; said bottom having a bevelled peripheral surface;and said side wall means being characterized by a downwardly slopingdiverging bevelled peripheral surface adapted to removably mate withsaid bevelled surface of said bottom of said ladling crucible.
 17. Anapparatus according to claim 16 wherein said material is ceramic foam.18. An apparatus according to claim 17 wherein said ceramic foammaterial has an air permeability in the range of 400 to 8,000 × 10⁻⁷cm², a porosity of 0.80 to 0.95 and a pore size of 5 to 45 pores perlinear inch.
 19. An improved ladling crucible for use in the filtrationof molten metal in which at least a part of said ladling crucible isformed of a material having an open cell structure characterized by aplurality of interconnected voids wherein said ladling crucible includesmeans to allow said ladling crucible to vertically slide on a support.20. The ladling crucible of claim 19 wherein said means is in the formof a track.
 21. An improved ladling crucible for use in the filtrationof molten metal in which at least a part of said ladling crucible isformed of a material having an open cell structure characterized by aplurality of interconnected voids wherein said crucible comprises amember having an open top, side wall means and a bottom, said open topbeing formed of an imperforated material and said side wall means andsaid bottom are formed of said material of open cell structure.
 22. Aladling crucible according to claim 21 wherein said material is ceramicfoam.
 23. An improved ladling crucible for use in the filtration ofmolten metal in which at least a part of said ladling crucible is formedof a material having an open cell structure characterized by a pluralityof interconnected voids, said crucible comprises a member having an opentop, side wall means and a bottom, wherein said open top has a bevelledperipheral surface and said side wall means has a bevelled peripheralsurface adapted to removably mate with said bevelled surface of saidopen top.
 24. A ladling crucible according to claim 23 wherein said opentop includes a resilient seal means on said bevelled wall surface. 25.An improved ladling crucible for use in the filtration of molten metalin which at least part of said ladling crucible is formed of a materialhaving an open cell structure characterized by a plurality ofinterconnected voids, said crucible comprises a member having an opentop, side wall means and a bottom wherein said side wall means has adownwardly sloping diverging bevelled peripheral surface and said bottomhas a bevelled peripheral surface adapted to removably mate with saiddiverging bevelled surface on said side wall means.